Correlation Between the XPS Peak Shapes of Y1Bu2Cu3O7-x and Film Quality
Document Type
Conference Proceeding
Publication Date
6-2003
Abstract
X-ray photoelectron spectroscopy (XPS) depth profiling was used to investigate the compositional and chemical profile of a typical YBCO coated conductor architecture. Results of the process revealed that the Y(3d) photoelectronic peak shape in these films is very different from bulk YBCO. To investigate this, several samples of Y1Ba2Cu3O7-x thin films were intentionally created of varying quality. The films were deposited on LaAlO3 by pulsed laser deposition with J(c) values ranging from poorly conducting up to several MA/cm(2). Initial results indicated a potential correlation between the Y(3d) XPS peak shape (full-width-half-maximum) of the YBCO and the film quality. A potential correlation may also exist with the Cu(2p)/Ba(3d) ratio indicating an interrelationship to the FWHM of the Y(3d) peak.. Film quality. was determined by current transport, resistive T-c, and AC magnetic susceptibility measurements.
Repository Citation
Mukhopadhyay, S. M.,
Barnes, P. N.,
Haugan, T. J.,
Krishnaswami, S.,
Tolliver, J. C.,
& Maartense, I.
(2003). Correlation Between the XPS Peak Shapes of Y1Bu2Cu3O7-x and Film Quality. IEEE Transactions on Applied Superconductivity, 13 (2), 3643-3646.
https://corescholar.libraries.wright.edu/mme/18
DOI
10.1109/TASC.2003.812419